Description: S2S PLID Thin Film polar bonds to metal surfaces providing a long lasting, self-healing fluid, thin film. It penetrates and de-scales existing rust, loosens and lubricates seized parts, and has a high dielectric strength of over 40 kV that prevents electrolysis.
S2S PLID Thin Film is applied by roller, brush, spraying or dunking. It can be applied to damp, painted and rusted surfaces and requires no sandblasting or curing time.
Application: Shake or stir product before use.
- Calculate product requirement: Coverage per gallon of product at 2 mils = 200 sq ft.
surface area. - Prepare surface by removing dirt, debris and degreaser. No sandblasting required. Can be applied over damp, rusted and painted surfaces.
- Spray, brush or roll product on evenly ensuring welds, cracks and corners are wellcoated. No curing time.
- Reapply when treated surface is dry to the touch or no longer shiny. Painting over S2S products is not recommended as paint may not adhere properly.
Removal: Product does not typically need to be removed but if desired, simply wash with a high pH detergent and water.
Disposal: Dispose of contents and container in accordance with applicable regional, national and local laws and regulations.
Storage: Store in a well-ventilated place at room temperature. Shelf life is greater than 2 years.
Clean up: Pour all remaining product back into container and cover. Use warm water and a high pH detergent to thoroughly clean spray equipment. If spray equipment will be used for another application of S2S products, a thorough cleaning of the lines is not necessary. However, if spray equipment will be going into storage, clean thoroughly and allow soapy water to remain in lines in order to avoid clogging.
Data Specifications:
| Base Type | Petroleum |
| Viscosity | 33 cSt at 40°C (104°F) |
| Relative Density | 0.869 (Water = 1) at 15.6 °C (60.1 °F) (ASTM D4052) |
| Burning Characteristics | 40.64kV (ASTM D877) |
| Dielectric | 40.64kV (ASTM D877) |
| Flash Point | 154°C (309.2°F) (ASTM D92) |
| Pour Point | -24°C (-11.2°F) (ASTM D97) |
| VOC content, wt.% | 0.1% |
| Last Non-Seizure Load (LNSL) | Last Non-Seizure Load (LNSL) |
| Weld Point | 250 kg (ASTM D2783) |
| Load Wear Index (LWI) | 38.25 (ASTM D2783) |
| Rust Protection Humidity Cab. | 100 hrs (ASTM D665) |