Polyimide Kapton film Silicon Tape by Tenacious Tapes. Adhesive tape comparable to 3M Polyester Tape 5413, Tesa 4428, Husky 23 or Nito Polyimide adhesive tape NO.360A. Order online from exclusive approved supplier Wayout Evacuation Systems.
Colour: Amber
Roll Size: 6mm to 1000mm in 33 Metre Lengths
Adhesive: Silicon
Description: Manufactured from commercial grade polyimide film with high performance silicone adhesive. Providing excellent protection for gold contacts of PCB during wave soldering and hot air levelling process. Also designed for uses in insulating coil at high temperature and for the applications of generator, capacitor, transformer and others. Excellent resistance to acid, oil, solvent & staining.
Application:
High temperature masking medium in powder coating applications
Masking of printed circuit boards during solder
Splicing of high temperature films
Tabbing ends of non-adhesive Kapton in field and armature coils
Technical Details:
| Thickness: | 0.06mm |
| Breaking Load: | 53 N/cm |
| Adhesion to Steel: | 2.2 N/cm |
| Elongation at Break: | 60% |
| Dielectric Strength: | 7000 volts |
| 90° Tack: | 1.1 N/cm |
| Service Temperature: | 0°C to +160°C |
| Storage Temperature: | 15°C to 25°C |
| Shelf Life: | 12 Months |
Surface Preparation: The surface on which the tape is to be used must be clean, dry and free from grease and dust. Remember that pressure sensitive adhesive must be applied with the maximum possible pressure in order to achieve maximum adhesion levels. The recommended application temperature is between 15ºC and 25ºC.
Storage: Tapes stored below the minimum application temperature will require warming up to that level before use. Up to 24 hours may be required for this to take place.
Note: The above figures represent average values. Actual figures can vary. The selection and
application of a tape is the responsibility of the buyer. Tape should be stored at room
temperature and should not be exposed to sunlight. We reserve the right to make changes
without notice to our products and specifications.